采用聚乙烯醇(PVA)、柠檬酸和六亚甲基四胺作为络合剂的溶胶凝胶法制备纳米阴极粉体La1–xSrxCo1–yFeyO3(LSCF)。用X射线衍射、透射电子显微镜和激光粒度仪分别对LSCF(x=0.4,y=0.6)粉体的晶型、结构和粒径分布进行了表征。采用丝网印刷法将LSCF(x=0.4,y=0.6)浆料印刷在具有阴极氧化钇掺杂氧化铈(gadolinium doped ceria,GDC)阻挡层的半电池上,经1000℃焙烧制成单电池。用扫描电子显微镜、压汞仪和电化学工作站等表征手段对单电池结构及其电性能等进行了表征。结果表明:前驱物经900℃煅烧获得斜方六面体晶系钙钛矿晶体结构阴极粉体LSCF,其分散度较高,颗粒形状较规则,一次粒子大小为50nm左右,用该阴极粉体LSCF(x=0.4,y=0.6)制备的单电池以H2+3%水蒸气为燃料气,空气为氧化气,在750℃时的最大功率密度为1.09W/cm2,欧姆电阻为0.17 cm2,极化电阻为0.61 cm2。
Abstract：A nano-powder of La1–xSrxCo1–yFeyO3(LSCF) cathode was perpared by the sol–gel method with PVA,citric acid and hexa-methylene tetramine as complexing agents.The crystalline phase,structure and particle size distribution were characterized by X-ray diffraction,transmission electron microscopy and Laser particle size analysis,respectively.The single cell via screen printing the LSCF(x = 0.4,y = 0.6) powder on an anode support half cell with a gadolinium doped ceria(GDC) barrier layer was fabricated at 1 000 ℃.The structure and performance of the single cell were characterized by scanning electron microscopy,mercury porosimetry and electrochemical workstation.The well-dispersive LSCF(x=0.4,y=0.6) powder with the rhombic hexahedron perovskite structure and the particle size of < 50 nm was obtained after calcining at 900 ℃.The maximum power density of single cell is 1.09 W/cm2,the ohmic resistance is 0.17 Ω?cm2 and the polarization resistance is 0.61 Ω?cm2 when H2+3%H2O as anode gas and air as cathode gas are used.
[1]余永志,罗凌虹,吴也凡,等.PMMA含量对水系流延IT-SOFC性能的影响[J].中国陶瓷,2012,48(3):13–16.YU Yongzhi,LUO Linghong,WU Yefan,et al.China Ceram(in Chi-nese),2012,48(3):13–16.
[2]谢笑虎,孙加林,宋文,等.Gd2O3掺杂ZrO2固体电解质材料的局域结构分析[J].硅酸盐学报,2011,39(8):1312–1316.XIE Xiaohu,SUN Jialin,SONG Wen,et al.J Chin Ceram Soc,2011,39(8):1312–1316.
[3]LIU Mingfei,DONG Ding,KEVIN Blinn,et al.Enhanced perform-ance of LSCF cathode through surface modification[J].Int J HydrogenEnergy,2012,37(10):8613–8620.
[4]张小珍,汪永清,周健儿,等.以Ni-YSZ和Sm0.5Sr0.5Fe0.8Cu0.2O3δ为电极的微管固体氧化物燃料电池的制备及电化学性能[J].硅酸盐学报,2012,40(8):1210–1214.ZHANG Xiaozhen,WANG Yongqing,ZHOU Jian’er,et al.J ChinCeram Soc,2012,40(8):1210–1214.
[5]FU Changjing,SUN Kening,ZHANG Naiqing,et al.Electrochemicalcharacteristics of LSCF-SDC composite cathode for intermediate tem-perature SOFC[J].Electrochim Acta,2007,52(13):4589–4594.
[6]林冬,王群浩,彭开萍.固体氧化物燃料电池复合电解质粉体BaCe0.8Y0.2O3–δ–Ce0.8Gd0.2O1.9的制备及表征[J].硅酸盐学报,2012,40(6):752–757.LIN Dong,WANG Qunhao,PENG Kaiping.J Chin Ceram Soc,2012,40(6):752–757.
[7]王小连,丁岩芝,林彬,等.中温固体氧化物燃料电池SmBaCo2O5+δ–Sm0.2Ce0.8O1.9复合阴极材料的电化学性能[J].硅酸盐学报,2012,40(10):1524–1529.WANG Xiaolian,DING Yanzhi,LIN Bin,et al.J Chin Ceram Soc,2012,40(10):1524–1529.
[8]LIU Jingbo,CO ANNE C,PAULSON Scott,et al.Oxygen reduction atsol–gel derived La0.8Sr0.2Co0.8Fe0.2O3 cathodes[J].Solid State Ionics,2006,177(3/4):377–387.
[9]SHAO Zongping,ZHOU Wei,ZHU Zhonghua.Advanced synthesis ofmaterials for intermediate-temperature solid oxide fuel cells[J].Pro-gress Mater Sci,2012,57(4):804–874.
[10]LETILLY M,JOUBERT O,SALLE A Le Gal La.Characterisation andoptimisation of the cathode/electrolyte couple for SOFC LSCF/BIT07[J].J Power Sources,2012,212:161–168.
[11]LETILLY M,JOUBERT O,SALLE A Le Gal La.Characteristics andperformance improvement of anode supported solid oxide fuel cellsbased on BaIn0.3Ti0.7O2.85(BIT07)as electrolyte,BIT07-Ni as anodeand La0.58Sr0.4Co0.2Fe0.8O3–1(LSCF)as cathode[J].J Power Sources,2012,206:210–214.
[12]ATANU DUTTA,JAYANTA MUKHOPADHYAY,R N BASU.Com-bustion synthesis and characterization of LSCF-based materials ascathode of intermediate temperature solid oxide fuel cells[J].J EurCeram Soc,2009,29(10):2003–2011.
[13]LEANDRO DA CONCEICAO,AMANDA M SILVA,NIELSON F PRIBEIRO,et al.Combustion synthesis of La0.7Sr0.3Co0.5Fe0.5O3(LSCF)porous materials for application as cathode in IT-SOFC[J].Mater ResBull,2011,46:308–314.
[14]BAI Yaohui,LIU Mingfei,DONG Ding,et al.Electrical and electro-catalytic properties of a La0.8Sr0.2Co0.17Mn0.83O3–1cathode for intermediate-temperature solid oxide fuel cells[J].J Power Sources,2012,205:80–85.
[15]HARDY JOHN S,TEMPLETON JARED W,EDWARDS DAN J,et al.Lattice expansion of LSCF-6428 cathodes measured by in situ XRDduring SOFC Operation[J].J Power Sources,2012,198:76–82.
[16]田晓利,薛群虎,薛崇勃.溶胶–凝胶法制备氧化铝–氧化锆复合粉体[J].硅酸盐学报,2012,40(6):866–871.TIAN Xiaoli,XUE Qunhu,XUE Chongbo.J Chin Ceram Soc,2012,40(6):866–871.
[17]王剑,邵刚勤,余晓华,等.Ce1–xGdxO2–x/2粉末的柠檬酸盐法合成及其固体氧化物燃料电池阳极的叠层法制备[J].硅酸盐学报,2011,39(4):563–567.WANG Jian,SHAO Gangqin,YU Xiaohua,et al.J Chin Ceram Soc,2011,39(4):563–567.
[18]石纪军,吴也凡,罗凌虹,等.沉淀法制备草酸镍对SOFC阳极电性能的影响[J].陶瓷学报,2011,32(3):381–384.SHI Jijun,WU Yefan,LUO Linghong,et al.J Ceram(in Chinese),2011,32(3):381–384.
[19]WANG Chengcheng,LUO Linghong,WU Yefan,et al.A novel multi-layer aqueous tape casting method for anode-supported planar solidoxide fuel cell[J].Mater Lett,2011,65:2251–2253.
[20]LUO Linghong,LANG Ying,HUANG Zuzhi,et al.Fabrication ofYSZ Film by Aqueous Tape Casting Using PVA-B1070 Cobinder forIT-SOFC[J].Key Eng Mater,2010,434/435:735–738.
[21]程亮,罗凌虹,吴也凡,等.阳极支撑结构IT-SOFC的阳极及电解质层的水系流延与共烧[J].陶瓷学报,2009,30(4):438–443.CHENG Liang,LUO Linghong,WU Yefan,et al.J Ceram(in Chi-nese),2009,30(4):438–443.
[22]WU Yefan,CHEN Hualong,HUANG Zuzhi,et al.Fabrication ofNi-based Anode Supported SOFCs by Aqueous Tape Casting[J].KeyEng Mater,2008(368–372):284–286.
[23]PIAO Jinhua,SUN Kening,ZHANG Naiqing,et al.A study of processparameters of LSM and LSM–YSZ composite cathode films preparedby screen-printing[J].J Power Sources,2008,175(1):288–295.
[24]CHEN Jing,LIANG Fengli,LIU Lina,et al.Nano-structured(La,Sr)(Co,Fe)O3+YSZ composite cathodes for intermediate temperaturesolid oxide fuel cells[J].J Power Sources,2008,183:586–589.
[25]LAI BO-KUAI,KERMAN K,RAMANATHAN S.NanostructuredLa0.6Sr0.4Co0.8Fe0.2O3/Y0.08Zr0.92O1.96/La0.6Sr0.4Co0.8Fe0.2O3(LSCF/YSZ/LSCF)symmetric thin film solid oxide fuel cells[J].J Power Sources,2011,196:1826–1832.
[26]FAN Baoan,YAN Jiabao,YAN Xiaochao.The ionic conductivity,thermal expansion behavior,and chemical compatibility of La0.54Sr0.44 Co0.2Fe0.8O3–δas SOFC cathode material[J].Solid State Sci,2011,13:1835–1839.
基本信息:
DOI：
中图分类号:TM911.4
引用信息:
[1]石纪军,吴也凡,罗凌虹等.溶胶-凝胶法制备固体氧化物燃料电池阴极粉体La_(0.6)Sr_(0.4)Co_(0.4)Fe_(0.6)O_3及其电性能[J].硅酸盐学报,2013,41(07):944-949.
基金信息:
国家自然科学基金(51162014,51262010);; 江西省青年科学基金(20114BAB216019);; 江西省重大科技创新研究项目(20114ACE00300)