以板状刚玉为骨料,莫来石为结合相,采用反应烧结工艺制备莫来石结合刚玉质耐火材料。以SiO2微粉作为合成莫来石的硅源,并尝试引入硅溶胶,以其部分取代SiO2微粉,旨在提高复相耐火材料的力学性能。结果表明:引入硅溶胶能促进莫来石合成,使显微结构更均匀致密,显著提高了材料强度和高温抗蠕变性。1550℃烧成时,以硅溶胶取代4%(质量分数,下同)SiO2微粉作硅源制备的样品比以SiO2微粉作硅源制备的样品,其常温和高温抗弯强度分别提高40.16%和29.92%;1650℃烧成时,前者比后者高温抗蠕变率降低71%。载荷-变形测试结果显示:莫来石结合刚玉质耐火材料常温断裂过程为渐进式,引入硅溶胶,在一定程度上提高了材料常温断裂韧性。
Abstract：Mullite bonded corundum refractory was synthesized by the reaction sintering technique and using tabular corundum as the aggregate and mullite as the bonding phase,and silica powders and silica sol were used as the SiO2 sources.The results show that the microstructure and properties of the refractory prepared using silica sol to partially substitute for silica powders as the SiO2-containing raw material can be improved;for example,the formation of mullite is accelerated,the uniformity and density are enhanced,and the strength and the high temperature creep resistance are improved.Compared with the sample using silica powders as the raw material,the room temperature and high temperature flexural strengths of the sample sintered at 1 550 ℃ using silica sol to replace 4%(in mass)silica powders are 40.16% and 29.92% higher,respectively,and the high temperature creep rate of the sample is 71% lower for the sample sintered at 1 650 ℃.The load-flexivity curves of the samples show that the fracture behavior of mullite bonded corundum refractory at room temperature is gradual,and adding silica sol can improve the fracture toughness of the refractory.
[1]MONTES O B,NIETO M I,MORENO R.Mullite compacts obtained by colloidal filtration of alumina powders dispersed in colloidal silica suspensions[J].Ceram Int,(in the press).
[2]LEE J E,KIM J W,JUNG Y G,et al.Effects of precursor pH and composition on the grain morphology and size of mullite ceramics in aqueous system[J].Mater Lett,2003,57:3239-3244.
[3]OHIRA H,ISMAIL M G M U,YAMAMOTO Y,et al.Mechanical properties of high purity mullite at elevated temperatures[J].J Eur Ceram Soc,1996,16:225-229.
[4]SACKS M D,BOZKURT M,SCHEIFFELE G W.Fabrication of mullite-matrix composites by transient viscous sintering of composite powders[J].J Am Ceram Soc,1991,74(1):2428-2437.
[5]KARA F,LITTLE J A.Sintering behaviour of precursor mullite pow-ders and resultant microstructures[J].J Eur Ceram Soc,1996,16:627-635.
[6]SIMENDIC B,RADONJIC L.Low temperature transformation of alumina-silicate gels[J].Ceram Int,1998,24:553-557.
[7]KONG D,YANG H,WEI S,et al.Gel-casting without de-airing proc-ess using silica sol as a binder[J].Ceram Int,2007,33:133-139.
[8]EVANKOVIC H,TKALCEC E,NASS R,et al.Correlation of the precursor type with densification behavior and microstructure of sin-tered mullite ceramics[J].J Eur Ceram Soc,2003,23:283-292.
[9]GHOSH S,MAJUMDAR R,SINHAMAHAPATRA B K,et al.Micro-structures of refractory castables prepared with sol-gel additives[J].Ceram Int,2003,29:671-677.
[10]STUDART A R,ORTEGA F S,INNOCENTINI M D M,et al.Gel casting high alumina refractory castables[J].Am Ceram Soc Bull,2002,81(2):42-48.
[11]OSENDI M I,BAUDIN C.Mechanical properties of mullite materials[J].J Eur Ceram Soc,1996,16:217-224.
[12]LIDEN E,KARLSSON S,TOKARZ B.Silica sols as refractory fibre binders[J].J Eur Ceram Soc,2001,21:795-808.
[13]朱新文,江东亮,谭寿洪,等.氧化铝粉体在硅溶胶中分散行为的研究[J].硅酸盐学报,2001,29(3):263-266.ZHU Xinwen,JIANG Dongliang,TAN Shouhong,et al.J Chin Ceram Soc(in Chinese),2001,29(3):263-266.
[14]高宝玉,李翠平.铝离子与聚硅酸相互作用[J].环境化学,1993,12(4):268-269.GAO Baoyu,LI Cuiping.Environ Chem(in Chinese),1993,12(4):268-269.
[15]张清纯.陶瓷材料的力学性能[M].北京:科学出版社,1987,316-320.ZHANG Qinchun.Mechanical Properties of Ceramics(in Chinese),Beijing:Science Press,1987.316-320.
[16]洪彦若,孙加林,王玺堂,等.非氧化物复合耐火材料[M].北京:冶金工业出版社,2003.8-9.HONG Yanruo,SUN Jialin,WANG Xitang,et al.Nonoxide Composite Refractory(in Chinese).Beijing:Metallurgy Press,2003.8-9.
[17]黄福明,袁荞龙,胡春圃,等.纳米二氧化硅水分散体的制备及复配[J].华东理工大学学报,2003,29(6):583-586.HUANG Fuming,YUAN Qiaolong,HU Chunpu,et al.J East China Univ Sci Technol(in Chinese),2003,29(6):583-586.
[18]IM S H,HERRICKS T.Synthesis and characterization of monodis-perse silica colloids loaded with super paramagnetic iron oxide nanoparticles[J].Chem Phys Lett,2005,401:19-23.
[19]SURATWALA T,HANNA M L,WHITMAN P.Effect of humidity during the coating of St?ber silica sols[J].J Non-Cryst Solids,2004,349:368-376.
[20]CHEN Z,ZHANG L,CHENG L,et al.Novel method of adding seeds for preparation of mullite[J].J Mater Process Technol,2005,166:183-187.
[21]DURAN C,TUR Y K.Templated grain growth of textured mul-lite/zirconia composites[J].Mater Lett,2005,59:245-249.
[22]KARA F,SENER O.Improvement of sintering and microstructural homogeneity of a diphasic mullite[J].J Eur Ceram Soc,2001(21):901-905.
[23]IWAHIRO T,NAKAMURA Y.Crystallization behavior and character-istics of mullites formed from alumina-silica gels prepared by the geopolymer technique in acidic conditions[J].J Eur Ceram Soc,2001,21:2515-2519.
[24]桂明玺.采用纳米技术开发耐火材料[J].国外耐火材料,2005,30(1):1-6.GUI Mingxi.Foreign Refractories(in Chinese),2005,30(1):1-6.
[25]芦贻春,李再耕.pH值对硅溶胶凝胶化过程的影响[J].耐火材料,1995,29(6):326-328,335.LU Yichun,LI Zaigeng.Refractories(in Chinese),1995,29(6):326-328,335.
基本信息:
DOI：
中图分类号:TQ175.1
引用信息:
[1]蔡艳芝,杨彬,王刚.硅溶胶对莫来石结合刚玉质耐火材料力学性能的影响[J].硅酸盐学报,2007,No.216(05):664-670.
基金信息: